Poly(ethylene) CAS NO.9002-88-4

Specifications1.VirginorRecyclePE(HDPE,LDPEorLLDPE) 2.CanbeusedforPEfilm,shoppingbag(blowing),(injection)andsoon ParticleHDPE 1.P…

 Specifications 1.Virgin or Recycle PE(HDPE,LDPE or LLDPE) 
2.Can be used for PE film,shopping bag (blowing),(injection) and so on

Particle HDPE
1.Product description
Technical specifications(HDPE) 
Film Grade

Item
 Test condition
 Test Method
 Value
 Unit
 
Density
  
 ISO 1183
 0.944-0.955
 g/cm3
 
MFR
 190°C/2.16kg
 ISO 1133
 0.03-0.07
 g/10min
 
Tensile strength at yield
  
 ISO 527-2
 22
 MPa
 
Elongation at break
  
 ISO 527-2 
 >350
 %
 
ESCR
 F50,50°C,100%
 ASTM D-1693A
 1000
 h
 
VICAT 
  
 ASTM D-1525
 126
 °C 
 

Blown Grade

Item
 Test Condition
 Test Method
 Value
 Unit
 
Density
  
 ISO 1183
 0.950~0.955 
 g/cm
 
MFR
 190°C/2.16kg
 ISO 1133
 1.7~2.5 
 g/10min
 
Tensile strength at yield
  
 ISO 527-2
 24
 MPa
 
Elongation at break
  
 ISO 527-2
 >600
 %
 

Injection grade

Item
 Test Condition
 Test Method
 Value
 Unit
 
MFR
 190°C/2.16kg
 ASTM D-1238
 20
 g/10min
 
Density
 ---
 ASTM D-792
 0.954
 g/cm3
 
Tensile strength at yiled
 ---
 ASTM D-638
 28
 MPa
 
Elongation at break
 ---
 ASTM D-638
 250
 %
 
Impact tensile strength
 ---
 ASTM D-1822
 42
 kJ/m2
 
ESCR
 

 ASTM D-1693
 3
 ---
 
VACIT
 ---
 ASTM D-1525
 127
 °C 

2.Application 

  HDPE (high density PE) - is used in products and packaging such as plastic bags, milk jugs, detergent bottles, margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams.